PRODUCTS UHMWPE / PE1000
OUTSTANDING APPLICATION PROPERTIES
EXCELLENT IMPACT RESISTANCE
LOW STATIC AND DYNAMIC FRICTION COEFFICIENT
HIGH WEAR RESISTANCE
HIGH WEATHERING RESISTANCE
HIGH TENACITY AND COMPRESSIVE STRENGTH
FOODSAFE & PHARMA GRADES
DELIVERY PROGRAM, all dimensions in mm
Standard Colors : Natural white, Black, Green, Blue, Red, Yellow
EXTRUDED RODS |
Mol. Wt 9.0 |
15 TO 90 DIA X 2000 LONG 100 TO 300 DIA X 1000 LONG |
PRESSED SHEETS |
5.0 |
8 TO 300 THICK X 1000 X 2000 8 TO 300 THICK X 1500 X 3000 / 1300 X 5000 / 2000 X 4500 - SPECIAL PRODUCTION WITH MOQ |
SKIVED SHEETS |
5.0 |
1 ,2, 3, 4, 5 THICK X 1000 X 2000 |
EXTRUDED / PRESSED HOLLOWS |
5.0 |
SPECIAL PRODUCTIONON REQUEST WITH MOQ0 |
CUSTOM SIZES |
5.0 / 9.0 |
RODS, SHEETS, HOLLOWS AVAILABLE ON REQUEST WITH MOQ |
MACHINED PARTS CIRCULAR |
9.0 |
10 TO 300 DIA |
MACHINED PARTS SQUARE /RECTANGULAR |
5.0 |
UPTO SIZES 2000 X 4500 OR 1300 X 5000 |
TECHNICAL DATA SHEET , MIN .MOL. WT5.0 MILLION
PROPERTY |
STANDARD |
VALUE |
|---|---|---|
Density |
ASTM D792 |
0.93-0.95 g/cm3 |
Water Absorption |
ASTM D570 |
<_0.01 % |
Tensile strength |
ASTM D638 |
≥18N/mm2 |
Elongation |
ASTM D638 |
≥50 % |
Impact strength, Izod,23�C |
ASTM D256 |
.100J/cm |
Hardness |
ASTM 785 |
61-65 Shore D |
Compressive strength at 1% def. |
ASTM D695 |
70 - 80 kg/cm2 |
Thermal conductivity |
ASTM D2214 |
0.41W/m. K |
Volume resistivity, at 50% RH |
ASTM D257 |
<105Ohm cm |
Surface resistivity , at 50% RH |
ASTM D257 |
<105Ohm |
Safe Operating temperatures |
- |
- 80 to +80 deg C |
Coefficient of friction, static |
ASTM D3028 |
≥ 0.2 |
Coefficient of friction, dynamic |
ASTM D3028 |
≥ 0.15 |
Moisture / solvent absorption |
- |
Negligible |
Combustibility |
- |
Partly non-combustible |
Weather resistance |
- |
Excellent |
TECHNICAL DATA SHEET , MIN .MOL. WT 9.0 MILLION
PROPERTY |
STANDARD |
VALUE |
|---|---|---|
Suitable for Food Contact |
- |
Yes |
Density |
DIN EN ISO 1183 |
0.93 g/cm3 |
Flamability |
DIN 4102 |
B2 mm |
Flamability |
UL 94 |
HB |
Water Absorption Rate |
DIN EN ISO62 |
<0.01 % |
Yield Stress / Tensile Strength |
DIN EN ISO 527-1 |
20 N/mm2 |
Elongation at Break |
DIN EN ISO 527-1 |
>200 % |
Tensile Modulus of Elasticity |
DIN EN ISO 527-1 |
680 N/mm2 |
Notched Impact Strength Charpy |
DIN EN ISO179.2 |
- mJ/mm2 |
Notched Impact Strength (Double) V Notch |
DIN EN ISO 179.2 |
>130 mJ/mm2 |
Shore - D Hardness |
DIN EN ISO 868/ 15 |
63 |
Melting Temperature |
DIN EN ISO 3146 |
135 Deg C |
Thermal Conductivity |
ISO 8302 |
0.4 W/m.k |
Specific Thermal Capacity |
DIN 51005 |
1.9 J/k.kg. |
Coefficient of Linear Thermal Expansion |
DIN 53752 |
150 � 230 1/K.106 |
Service Temperature Long Term |
- |
- 250 to 80 Deg C |
Service Temperature Short Term |
- |
130 Deg C |
Heat Deflection Temperature |
DIN EN ISO 306 VICAT A |
Deg C |
Heat Deflection Temperature |
DIN EN ISO 306 VICAT B |
79 Deg C |
Dielectric Constant |
DIN VDE 0303-4 |
2.3 |
Di-electric Dissipation Factor |
DIN VDE 0303-4 |
1 x 1014 |
Specific Volume Resistivity |
DIN VDE 0303-3 |
>1014 Ohm/scm |
Surface Resistivity |
DIN VDE 0303-3 |
>1014 Ohm |
Comparative Tracking Index (Test Solution A) |
IEC 60112 |
600 CTI |
Di-electric Strength |
IEC 60243 |
45 KV/mm |
DISCLAIMER
- THE VALUES GIVEN IN THE DATA SHEET ARE FOR REFERENCE ONLY.
- CUSTOMERS ARE ADVISED TO TEST THE SUITABILITY OF OUR MATERIALS FOR THEIR APPLICATION AS THESE VALUES MAY NOT DIRECTLY HOLD GOOD UNDER ALL COMPLEX / MULTIPLE APPLICATION CONDITIONS.
- OUR COMPANY DOES NOT UNDERTAKE ANY LIABILITY, DIRECT OR INDIRECT, LINKED WITH THE USAGE AND PERFORMANCE OF OUR MATERIALS UNDER APPLICATION CONDITIONS.
- CUSTOMERS ARE ADVISED TO TEST THE SUITABILITY OF OUR MATERIALS FOR THEIR APPLICATION AS THESE VALUES MAY NOT DIRECTLY HOLD GOOD UNDER ALL COMPLEX / MULTIPLE APPLICATION CONDITIONS.
- OUR COMPANY DOES NOT UNDERTAKE ANY LIABILITY, DIRECT OR INDIRECT, LINKED WITH THE USAGE AND PERFORMANCE OF OUR MATERIALS UNDER APPLICATION CONDITIONS.